Corrosion Mechanisms & Damage Assessment Flashcards

What is a common form of corrosion found in carbon steel pressure vessels?

Answer: Uniform corrosion

Uniform corrosion is a common form of degradation in carbon steel pressure vessels, where the entire exposed surface corrodes at a relatively consistent rate. This leads to a general thinning of the material over time, which can be monitored by thickness measurements.

Which mechanism best describes chloride-induced pitting in stainless steels?

Answer: Pitting corrosion

Chloride-induced pitting in stainless steels is a highly localized form of corrosion where the passive film breaks down in specific areas. This leads to the formation of small, deep holes or pits on the material surface, often in the presence of chloride ions and stagnant conditions.

Which environment is most likely to cause stress corrosion cracking (SCC)?

Answer: Chloride-rich and tensile stress conditions

Stress Corrosion Cracking (SCC) occurs when a susceptible material is exposed to a specific corrosive environment while under tensile stress. Chloride-rich environments are particularly known to induce SCC in many alloys, including stainless steels, when combined with sufficient tensile stress.

What is the most appropriate inspection technique for detecting internal corrosion?

Answer: Ultrasonic thickness testing

Ultrasonic thickness testing (UTT) is the most appropriate and widely used technique for detecting and quantifying internal corrosion. It works by sending sound waves into the material and measuring the time it takes for the echo to return, allowing for precise measurement of remaining wall thickness.

What type of damage is typically associated with hydrogen blistering?

Answer: Localized metal lifting and blister formation

Hydrogen blistering occurs when atomic hydrogen diffuses into the metal and recombines to form molecular hydrogen gas at internal discontinuities, such as laminations. The trapped hydrogen gas builds up pressure, causing localized bulging or lifting of the metal surface, forming blisters.

How can galvanic corrosion be mitigated?

Answer: Using sacrificial anodes

Galvanic corrosion occurs when two dissimilar metals are in electrical contact in an electrolyte. Using sacrificial anodes, which are made of a more active metal, protects the primary component by corroding preferentially, thereby mitigating the galvanic attack on the structure.

Which technique is used to identify corrosion under insulation (CUI)?

Answer: Radiographic or guided wave ultrasonic testing

Corrosion Under Insulation (CUI) is challenging to detect because it's hidden beneath insulation. Radiographic testing (RT) can image the internal condition through insulation, while guided wave ultrasonic testing (GWUT) can inspect long lengths of pipe or vessel walls from a single access point, making them effective for CUI detection.

What is the typical appearance of pitting corrosion?

Answer: Localized deep holes

Pitting corrosion is characterized by the formation of small, localized holes or cavities on the metal surface. These pits can be quite deep relative to their diameter, often leading to rapid penetration of the material even with minimal overall weight loss.

Which material is most resistant to corrosion in acidic environments?

Answer: Hastelloy

Hastelloy is a family of nickel-based alloys renowned for their exceptional corrosion resistance, particularly in harsh acidic and high-temperature environments. These alloys are specifically engineered to withstand aggressive chemical attack where other materials would fail.